Heat treating and quenching of steel generally makes it more ductile.

Hittebehandeling en blus van staal maak dit gewoonlik meer rekbaar.

When comparing brittle and ductile fracture, brittle fracture is generally characterised by a relatively higher impact energy at fracture while ductile fracture is characterised by a relatively lower impact energy at fracture.

By die vergelyking van bros en rekbare breuk word bros breuk oor die algemeen gekenmerk deur 'n relatief hoër slagenergie by breuk, terwyl rekbare breuk gekenmerk word deur 'n relatief laer slagenergie by breuk.

When comparing brittle and ductile fracture, brittle fracture is generally characterised by a relatively lower impact energy at fracture while ductile fracture is characterised by a relatively higher impact energy at fracture.

By die vergelyking van bros en rekbaar breuk, word bros breuk oor die algemeen gekenmerk deur 'n relatief laer slagenergie by breuk, terwyl rekbare breek gekenmerk word deur 'n relatief hoër slagenergie by breuk.

Brittle metals have a relatively high energy absorption before fracture.

Bros metale het 'n relatief hoë energie -opname voor breuk.

A ductile fracture surface is generally indicated by a large area of shear and exhibits substantial plastic deformation or necking. 

'n Rekbare breukoppervlak word gewoonlik aangedui deur 'n groot skuifvlak en vertoon aansienlike plastiese vervorming of nekking.

Heat treating and quenching of steel generally makes it more brittle.

Hittebehandeling en blus van staal maak dit gewoonlik meer bros.

A brittle fracture surface is generally indicated by clean, flat break and exhibits very little to no plastic deformation or necking. 

'n Bros breukoppervlak word gewoonlik aangedui deur 'n skoon, plat breuk en vertoon baie min tot geen plastiese vervorming of nekking.

Ductile metals have a relatively low energy absorption before fracture.

Rekbare metale het 'n relatief lae energie -opname voor breuk.