Generate and submit a figure suitable for determining and comparing the appropriate hardenability of the two alloys, using the hardenability data provided on STEMLearn (Practical Test Hardness Data.txt) and the correct answers to Questions 7 and 8. Remember to exclude values that are inaccurate. 

• Ensure that the graphed data points are clearly indicated and that the graph is clearly labelled, including chart title, axis labels, units and a legend
• Submit only one MS Excel file

  containing the following on the same sheet: 

  • The raw data 
  • Any processed data used to construct the curves
  • Both curves on a single figure

• Name your excel file as 'H_curve_excel_student_number.xlsx', where  "student_number" is your student number. For example, a student with the student number 12345678 will have a file named 'H_curve_excel_12345678.xlsx'.
• Note: the files will be checked for plagiarism. Do not copy anyone else's work. 
• Following instructions and being neat will count in your favour.

Maak en dien in 'n figuur in wat geskik is om die verhardbaarheid van die twee allooie te bepaal en te vergelyk, deur die toepaslike verhardbaarheidsdata wat op STEMLearn (Practical Test Hardness Data.txt) verskaf word en die korrekte antwoorde op Vraag 7 en 8 te gebruik. Onthou om waardes wat onakkuraat is uit te sluit.

• Maak seker dat die grafiekdatapunte duidelik aangedui word en dat die grafiek duidelik benoem is, insluitend grafiektitel, asbyskrifte, eenhede en 'n legende
• Dien slegs een MS Excel-lêer in wat die volgende op dieselfde blad bevat:Noem u Excel-lêer as 'H_kurwe_excel_studente_nommer.xlsx', waar "studente_nommer" u studentenommer is. Byvoorbeeld, 'n student met die studentenommer 12345678 sal 'n lêer met die naam 'H_curve_excel_12345678.xlsx' hê.

  • Die rou data
  • Enige verwerkte data wat gebruik word om die krommes te konstrueer
  • Albei kurwes op 'n enkele figuur

• Let wel: die lêers sal vir plagiaat nagegaan word. Moet nie iemand anders se werk kopieer nie.
• Om instruksies te volg en netjies te wees sal in u guns tel. 

For plotting your hardenability curve, you wish to substitute the missing hardness values ([did not measure]) with theoretical hardness values based solely on carbon composition and assuming 50% martensite (based on some micrographs that you observed at the location of the indentation with the missing value). Enter this value for the AISI 1060 steel alloy below. Do not forget units.

Vir die plot van u verhardbaarheidskurwe, wil u die ontbrekende hardheid waardes ([did not measure]) vervang met teoretiese hardheidwaardes wat uitsluitlik op koolstofsamestelling gebaseer is en wat 50% martensiet aanvaar (gebaseer op sommige mikrograwe wat u waargeneem het by die plek van die inkeping met die ontbrekende waarde). Voer hierdie waarde vir die AISI 1060 staalallooi hieronder in. Moet nie eenhede vergeet nie.

Which of the steel alloys (AISI 8640 vs AISI 1060) has a higher hardenability and why? / Watter van die staalallooie (AISI 8640 vs AISI 1060) het 'n hoër verhardbaarheid en hoekom?

Select the most likely reason for the differences between the hardness values measured from the first indentations (closest to the quenched end) for both alloys: / 

For the experimental data provided and the carbon composition, at what distance from the quenched end do you expect 50% martensite to form for the AISI 8640 steel alloy? Give the answer to 3 significant figures and remember units. / Vir die eksperimentele data verskaf en die koolstofsamestelling, op watter afstand vanaf die gebluste punt verwag u dat 50% martensiet sal vorm vir die AISI 8640 staalallooi? Gee die antwoord vir 3 betekenisvolle syfers en onthou eenhede.

Match the SEM micrographs of the surface microstructures with the most probable positions (distance from quenched end) for the AISI 1060 steel Jominy end-quench test specimen. 

Pas die SEM mikrograwe van die oppervlakmikrostrukture by die mees waarskynlike posisies (afstand vanaf uitgebluspunt) vir die AISI 1060 staal Jominy eindblustoetsstuk.

For plotting your hardenability curve, you wish to substitute the missing hardness values ([did not measure]) with theoretical hardness values based solely on carbon composition and assuming 100% martensite. Enter this value for the AISI 8640 steel alloy below. Do not forget units.

Vir die plot van u verhardbaarheidskurwe, wil u die ontbrekende hardheid waardes ([did not measure]) vervang met teoretiese hardheidwaardes wat uitsluitlik op koolstofsamestelling gebaseer is en wat 100% martensiet aanvaar. Voer hierdie waarde vir die AISI 8640 staalallooi hieronder in. Moet nie eenhede vergeet nie.

In which of the following cases should the Jominy end-quench test specimen be completely replaced and a new test be done? In other words, the same specimen cannot be reused at all. / In watter van die volgende gevalle moet die Jominy eindblustoetsstuk heeltemal vervang word en 'n nuwe toets gedoen moet word? Met ander woorde, dieselfde monster kan glad nie hergebruik word nie.

What was the indentation load is used for the hardness measurements made for the hardenability tests performed according to ASTM A255? 

Watter inkepingslading word gebruik vir die hardheidmetings wat vir die verhardbaarheids toetse uitgevoer word volgens ASTM A255? 

Choose the statements which are True.

Kies water van die stellings waar is.